| EMI/RFI
Coatings and Gaskets |
EMI/RFI
SHIELDED
COATINGS |
We offer the Isolex WP 120 nickel acrylic conductive coating as our standard EMI/RFI coating. Upon request we also have available Electro DAG 7050, copper acrylic conductive coating.
Detailed spec sheet is available upon request.
|
|
EMI/RFI
SHIELDED
STANDARD GASKETS |
All data supplied is from manufacturer’s engineering data sheets.
We offer the Cho-Seal 1350 gasket as our standard EMI/RFI gasket.
Cho-Seal is a silver-plated glass-filled material and will not remain sufficiently conductive during vibration or after EMP-induced currents. |
|
|
| |
Test
Standard |
Cho-Seal
1351 |
| Grade |
|
Industrial
Commercial |
| Elastomer
Binder |
|
Silicone |
| Conductive
Filler |
|
Ag/glass |
Volume
Resistivity
(ohm-cm, max) as supplied |
MIL-G-83528
Para 4.6.11 |
0.01 |
| Durometer
(shore A65) |
ASTM
D2240 |
65 |
| Specific
Gravity (60.2) |
ASTM
D792 |
1.8 |
| Tensile
Strength (psi, min.) |
ASTM
D412 |
150 |
| Elongation
(percent, min/max) |
ASTM
D 412 |
75/300 |
| Tear
Strength |
ASTM
D625 |
25 |
Compression
Set, 70 hrs. @ 100º C
(percent, max) |
ASTM
D395
Method B |
30 |
Low
Temperature Flex, TRIO
(ºC, minimum) |
ASTM
D1329 |
-55 |
Maximum
Continuous Use
Temperature (ºC) |
|
160 |
|
|
200
KHZ (H Field)
100 MHz (E Field)
500 MHz (E Field)
2 GHz (Plane Wave)
10 GHZ (Plane Wave)
|
|
MIL-G-83528
Para. 4.6.12
|
50
100
100
90
80
|
|
|
Heat
Aging |
|
MIL-G-83528
Para. 4.6.15 |
|
Vibration
Resistance |
During |
| After |
|
MIL-G-85328
Para. 4.6.13 |
N/A |
| N/A |
| Post
Tensile Strength |
MIL-G-83528
Para. 4.6.9 |
0.01
0.01 |
| EMP
Survivability (KA) |
MIL-G-83528
Para. 4.6.16 |
NS |
|
|
EMI/RFI
SHIELDED
OPTIONAL GASKETS
(SPECIAL ORDER
ONLY) |
| For
military requirements where greater
shielding is required, such as EMP
survivability, we can supply Cho-Seal
1285 gasket, which meets the Specs
listed below. Rose+Bopla DOES NOT stock
this gasket. Accordingly, we will have
to advise lead-time, delivery, cost and
minimum quantity (if applicable), if
Rose+Bopla is to supply this higher
grade gasket. |
|
|
| |
Cho-Seal
1285 |
Test
Standard |
| Grade |
|
Mil
Aerospace |
| Elastomer
Binder |
|
Silicone |
| Conductive
Filler |
|
Ag/A1 |
Volume
Resistivity
(ohm-cm, max) as supplied |
MIL-G-83528
Para 4.6.11 |
0.008 |
| Durometer
(shore A65) |
ASTM
D2240 |
65 |
| Specific
Gravity (60.2) |
ASTM
D792 |
1.9 |
| Tensile
Strength (psi, min.) |
ASTM
D412 |
200 |
| Elongation
(percent, min/max) |
ASTM
D 412 |
100/300 |
| Tear
Strength (lb./in., min.) |
ASTM
D624 |
30 |
Compression
Set, 70 hrs. @ 100º C
(percent, max) |
ASTM
D395
Method B |
32 |
Low
Temperature Flex, TRIO
(ºC, minimum) |
ASTM
D1329 |
-65 |
Maximum
Continuous Use
Temperature (ºC) |
|
200 |
|
|
200
kHZ (H Field)
100 MHz (E Field)
500 MHz (E Field)
2 GHz (Plane Wave)
10 GHZ (Plane Wave)
|
|
MIL-G-83528
Para. 4.6.12
|
60
115
100
105
100
|
|
|
Heat
Aging |
|
MIL-G-83528
Para. 4.6.15 |
0.01 |
Vibration
Resistance |
During |
| After |
|
MIL-G-85328
Para. 4.6.13 |
0.012 |
| 0.008 |
| Post
Tensile Strength |
MIL-G-83528
Para. 4.6.9 |
0.015 |
| EMP
Survivability (KA) |
MIL-G-83528
Para. 4.6.16 |
0.9 |
|
|
|
*
Maximum continuous use is defined as
1000 hours at max. rated temperature
(compressed between flanges 7-10%)
without electrical degradation above the
limits given under Electrical
Stability-Heat Aging.
|
CROSS
REFERENCE
CHART |
| Part
Number |
Gasket
Size |
| Metric |
Inches |
| 10082020
00 |
2.0mm |
.078 |
| 10082021
00 |
2.5mm |
.098 |
| 10082022
00 |
3.0mm |
.118 |
| 10082023
00 |
3.5mm |
.137 |
| 10082024
00 |
4.0mm |
.157 |
| 10082025
00 |
5.0mm |
.197 |
| 10082026
00 |
5.5mm |
.216 |
|
|
We have attempted to
present the information about our enclosures on
this website in a straight-forward manner. We
offer this information as accurate at the time of
publication. Specifications are subject to change
without notice. Rose+Bopla Enclosures is not
responsible for inadvertent errors. |
|
©2008 Phoenix Mecano Inc., 7330 Executive Way,
Frederick, MD 21704, 301-696-9800,
rbinfo@pm-usa.com |
|
|
|